La varmorezista ŝtala fosaĵo rilatas al ŝtalo kun alta temperatura rezisto kaj alta temperaturforto
High temperature antioxidant is an important condition to ensure that workpieces work at high temperature. In oxidation environments such as high -temperature air, a chemical response to the surface of oxygen and steel surface generates a variety of iron oxide layers. The oxide layer is very loose, loses the original characteristics of the steel, and it is easy to fall off. In order to improve the high temperature antioxidant of steel, Alaj elementoj estas aldonitaj al la ŝtalo por ŝanĝi la strukturon de oksidoj .
Common alloy elements include chromium, silicon, aluminum, etc. They react with oxygen to generate dense, stable oxide layers on the surface of the steel, or CR2O3, SIO2 or Al2O3, etc., to protect the steel no longer continue to oxidize. The amount of chromium, silicon, and aluminum adds a lot, and the high temperature of the steel is Pli bona . Tamen, se estas tro multe da silicio kaj aluminio, la mekanikaj proprietoj kaj proceso de ŝtalo difektos . Tial, varmorezistaj ŝtalaj fandejoj uzas kromon kiel ĉefan alojo -elementon kaj silicion kaj aluminion kiel helpajn elementojn .